High temperature self-lubricating NiAl matrix composites with addition of CuO (15, 20, and 25 wt.%) were fabricated by powder metallurgy technique, and the tribological behavior from room temperature to 1000 °C was investigated. It was found that Ni–Cu and Al2O3 phases formed during the fabrication process due to reaction of NiAl and CuO. The tribological results showed that the composite with addition of 25 wt.% CuO has a favorable friction coefficient of about 0.2 and excellent wear resistance with the magnitude of 10−6 mm3 N−1 m−1 at high temperatures (800 and 1000 °C).
Issue Section:
Friction and Wear
References
1.
Deevi
, S. C.
, Sikkat
, V. K.
, and Liu
, C. T.
, 1991
, “Processing, Properties, and Applications of Nickel and Iron Aluminides
,” Prog. Mater. Sci.
, 42
, pp. 177
–192
.2.
Yamaguchi
, M.
, Inui
, H.
, and Ito
, K.
, 2000
, “High Temperature Structural Intermetallics
,” Acta Mater.
, 48
(1
), pp. 307
–322
.3.
Czeppe
, T.
, and Wierzbinski
, S.
, 2000
, “Structure and Mechanical Properties of NiAl and Ni3Al-Based Alloys
,” Int. J. Mech. Sci.
, 42
(8
), pp. 1499
–1518
.4.
Bei
, H.
, and George
, E. P.
, 2005
, “Microstructures and Mechanical Properties of a Directionally Solidified NiAl-Mo Eutectic Alloy
,” Acta Mater.
, 53
(1
), pp. 69
–77
.5.
Johnson
, D. R.
, Chen
, X. F.
, Oliver
, B. F.
, and Noebe
, R. D.
, 1995
, “Whittenberger JD. Processing and Mechanical Properties of In-Situ Composites From the NiAl-Cr and the NiAl-(Cr, Mo) Eutectic Systems
,” Intermetallics
, 3
(2
), pp. 99
–113
.6.
Grabk
, H. J.
, Brumm
, M. W.
, and Wagemann
, B.
, 1996
, “The Oxidation of NiAl
,” Mater. Corros.
, 47
(12
), pp. 675
–677
.7.
Guo
, J. T.
, and Xu
, C. M.
, 2002
, “Effect of NiAl Microcrystalline Coating on the High-Temperature Oxidation Behavior of NiAl-28Cr-5Mo-1Hf
,” Oxid. Met.
, 58
(5), pp. 457
–468
.8.
Jin
, J. H.
, and Stephenson
, D. J.
, 1998
, “The Sliding Wear Behaviour of Reactively Hot Pressed Nickel Aluminides
,” Wear
, 217
(2
), pp. 200
–207
.9.
Hawk
, J. A.
, and Alman
, D. E.
, 1999
, “Abrasive Wear Behavior of NiAl and NiAl-TiB2 Composites
,” Wear
, 225–229
, pp. 544
–556
.10.
Lee
, H. Y.
, Roe
, J. K.
, and Ikenaga
, A.
, 2006
, “Sliding Wear Properties for Ni-Al Based Intermetallic Compound Layer Coated on Ductile Cast Iron by Combustion Synthesis
,” Wear
, 260
(1–2), pp. 83
–89
.11.
Johnson
, B. J.
, Kennedy
, F. E.
, and Baker
, I.
, 1996
, “Dry Sliding Wear of NiAl
,” Wear
, 192
(1–2), pp. 241
–247
.12.
Murakami
, T.
, Ouyang
, J. H.
, Sasaki
, S.
, Umeda
, K.
, and Yoneyama
, Y.
, 2005
, “High-Temperature Tribological Properties of Al2O3, Ni-20 Mass% Cr and NiAl Spark-Plasma-Sintered Composites Containing BaF2-CaF2 Phase
,” Wear
, 259
(1–6), pp. 626
–633
.13.
Jeng
, M. C.
, and Soong
, Y. L.
, 1993
, “Wear Behaviour of Solid Lubricants Ag and BaF2-CaF2 Obtained by Laser Surface Cladding
,” Surf. Coat. Technol.
, 57
(2–3), pp. 145
–150
.14.
Zhu
, S. Y.
, Bi
, Q. L.
, Yang
, J.
, and Liu
, W. M.
, 2011
, “NiAl Matrix High Temperature Self-Lubricating Composite
,” Tribol. Lett.
, 41
(3
), pp. 535
–540
.15.
Liu
, E.
, Gao
, Y.
, Bai
, Y.
, Yi
, G.
, Wang
, W.
, Zeng
, Z.
, and Jia
, J.
, 2014
, “Tribological Properties of Self-Lubricating NiAl/Mo-Based Composites Containing AgVO3 Nanowires
,” Mater. Charact.
, 97
, pp. 116
–124
.16.
Shi
, X.
, Zhai
, W.
, Wang
, M.
, Xu
, Z.
, Yao
, J.
, Song
, S.
, and Wang
, Y.
, 2014
, “Tribological Behaviors of NiAl Based Self-Lubricating Composites Containing Different Solid Lubricants at Elevated Temperatures
,” Wear
, 310
(1–2), pp. 1
–11
.17.
Li
, F.
, Cheng
, J.
, Qiao
, Z.
, Ma
, J.
, Zhu
, S.
, Fu
, L.
, Yang
, J.
, and Liu
, W.
, 2013
, “A Nickel-Alloy-Based High-Temperature Self-Lubricating Composite With Simultaneously Superior Lubricity and High Strength
,” Tribol. Lett.
, 49
(3
), pp. 573
–577
.18.
Zhu
, S. Y.
, Kong
, L. Q.
, Li
, F.
, Yang
, J.
, Ma
, J. Q.
, Cheng
, J.
, Zhen
, J. M.
, and Qiao
, Z. H.
, 2015
, “NiAl Matrix Self-Lubricating Composite at a Wide Temperature Range
,” ASME J. Tribol.
, 137
(2
), p. 021301
.19.
Spikes
, H.
, 2001
, “Tribology Research in the Twenty-First Century
,” Tribol. Int.
, 34
(12
), pp. 789
–799
.20.
Sliney
, H. E.
, 1982
, “Solid Lubricant Materials for High Temperatures-A Review
,” Tribol. Int.
, 5
, pp. 303
–315
.21.
Erdemir
, A.
, 2000
, “A Crystal-Chemical Approach to Lubrication by Solid Oxides
,” Tribol. Lett.
, 8
, pp. 97
–102
.22.
Peterson
, M. B.
, Murray
, S. F.
, and Florek
, J. J.
, 1959
, “Consideration of Lubricants for Temperatures Above 1000 °F
,” Tribol. Trans.
, 2
(2
), pp. 225
–234
.23.
Kerkwijk
, B.
, García
, M.
, Van
, Z. W.
, Winnubst
, L.
, Mulder
, E. J.
, Schipper
, D. J.
, and Verweij
, H.
, 2004
, “Friction Behaviour of Solid Oxide Lubricants as Second Phase in α-Al2O3 and Stabilised ZrO2 Composites
,” Wear
, 256
(1–2), pp. 182
–189
.24.
Ran
, S.
, Winnubst
, L.
, Blank
, D. H. A.
, Pasaribu
, H. R.
, Sloetjes
, J. W.
, and Schipper
, D. J.
, 2009
, “Dry-Sliding Self-Lubricating Ceramics: CuO Doped 3Y-TZP
,” Wear
, 267
(9–10), pp. 1696
–1701
.25.
Pasaribu
, H. R.
, Sloetjes
, J. W.
, and Schipper
, D. J.
, 2003
, “Friction Reduction by Adding Copper Oxide Into Alumina and Zirconia Ceramics
,” Wear
, 255
(1–6), pp. 699
–707
.26.
Pasaribu
, H. R.
, Reuver
, K. M.
, Schipper
, D. J.
, Ran
, S.
, Wiratha
, K. W.
, Winnubst
, A. J. A.
, and Blank
, D. H. A.
, 2005
, “Environmental Effects on Friction and Wear of Dry Sliding Zirconia and Alumina Ceramics Doped With Copper Oxide
,” Int. J. Refract. Met. Hard Mater.
, 23
(4–6), pp. 386
–390
.27.
Wahl
, K. J.
, Seitzman
, L. E.
, Bolster
, R. N.
, Singer
, I. L.
, and Peterson
, M. B.
, 1997
, “Ion-Beam Deposited Cu-Mo Coatings as High Temperature Solid Lubricants
,” Surf. Coat. Technol.
, 89
(3
), pp. 245
–251
.28.
Öztürk
, A.
, Ezirmik
, K. V.
, Kazmanlı
, K.
, Ürgen
, M.
, Eryılmaz
, O. L.
, and Erdemir
, A.
, 2008
, “Comparative Tribological Behaviors of TiN-, CrN- and MoN-Cu Nanocomposite Coatings
,” Tribol. Int.
, 41
(1
), pp. 49
–59
.29.
Erdemir
, A.
, 2005
, “A Crystal Chemical Approach to the Formulation of Self-Lubricating Nanocomposite Coatings
,” Surf. Coat. Technol.
, 200
(5–6), pp. 1792
–1796
.30.
Donnet
, C.
, and Erdemir
, A.
, 2004
, “Solid Lubricant Coatings: Recent Developments and Future Trends
,” Tribol. Lett.
, 17
(3
), pp. 389
–397
.31.
Zhu
, S. Y.
, Bi
, Q. L.
, Niu
, M. Y.
, Yang
, J.
, and Liu
, W. M.
, 2012
, “Tribological Behavior of NiAl Matrix Composites With Addition of Oxides at High Temperatures
,” Wear
, 274–275
, pp. 423
–434
.32.
Kong
, L. Q.
, Bi
, Q. L.
, Zhu
, S. Y.
, Qiao
, Z. H.
, Yang
, J.
, and Liu
, W. M.
, 2014
, “Effect of CuO on Self-Lubricating Properties of ZrO2(Y2O3)-Mo Composites at High Temperatures
,” J. Eur. Ceram. Soc.
, 34
(5
), pp. 1289
–1296
.33.
Li
, S. Z.
, Jiang
, X. X.
, Yin
, F. C.
, Peterson
, M. B.
, and Calabrese
, S. J.
, 1989
, “On Self-Lubricating Behavior of Ni-Cu-Re Alloy at Elevated Temperature
,” Chin. J. Mater. Res.
, 3
, pp. 481
–486
.34.
Jiang
, X. X.
, Li
, S. Z.
, Peterson
, M. B.
, and Calabrese
, S. J.
, 1989
, “On Self-Lubricating Behavior of Co-Cu-Re Alloys at Elevated Temperature
,” Chin. J. Mater. Res.
, 3
, pp. 487
–493
.35.
Peterson
, M. B.
, Calabrese
, S. J.
, and Stupp
, B.
, 1982
, “Lubrication With Naturally Occurring Double Oxide Films
,” Final Report, ONR Contract No. N00014-82-C-0247
.36.
Peterson
, M. B.
, Calabrese
, S. J.
, Li
, S. Z.
, and Jiang
, X. X.
, 1994
, “Friction of Alloys at High Temperature
,” J. Mater. Sci. Technol.
, 10
(5
), pp. 313
–320
.37.
Pauschitz
, A.
, Roy
, M.
, and Franek
, F.
, 2008
, “Mechanisms of Sliding Wear of Metals and Alloys at Elevated Temperatures
,” Tribol. Int.
, 41
(7
), pp. 584
–602
.38.
Stott
, F. H.
, 2002
, “High-Temperature Sliding Wear of Metals
,” Tribol. Int.
, 35
(8
), pp. 489
–495
.39.
Huai
, K. W.
, Guo
, J. T.
, Gao
, Q.
, Li
, H. T.
, and Yang
, R.
, 2007
, “Microstructure and Mechanical Behavior of NiAl-Based Alloy Prepared by Powder Metallurgical Route
,” Intermetallics
, 15
(5–6), pp. 749
–752
.Copyright © 2016 by ASME
You do not currently have access to this content.