Commercial pure titanium has been widely used in the aerospace, chemical, and biomedical industries because of its light weight, high corrosion resistance, high strength, high heat resistance, and good biocompatibility. Pure titanium takes the form of a hexagonal closed-pack structure with anisotropic elasticity and plasticity, with most of its components being polycrystalline aggregates having different crystal orientations. Small mechanical loading under elastic conditions therefore always induces inhomogeneous microscopic deformation, and the resulting inhomogeneity brings about various defects such as inhomogeneous plastic deformation, microcracking, and necking. It is therefore important to investigate the microscopic inhomogeneous deformation under elastic and plastic conditions. In this study, a plate specimen of commercial pure titanium was subjected to a tensile test on the stage of a digital holographic microscope (DHM), and the microscopic deformation of grains in the specimen under elastic and plastic conditions were observed and measured. During the test, the grains’ height distribution was measured in a fixed area on the specimen’s surface at each tensile loading step, and the correlation between height distributions at different loads was examined. We found from the measurements that each grain shows a different height change even under elastic conditions with a small load. This inhomogeneous height change was enhanced as the load was increased to plastic conditions. A strong correlation between the height changes under elastic and plastic conditions was also found. This result suggests that the microscopic deformation experienced under plastic conditions is predictable from that observed under elastic conditions.

References

1.
Banerjee
,
D.
, and
Williams
,
J. C.
,
2013
, “
Perspective on Titanium Science and Technology
,”
Acta Mater.
,
61
(
3
), pp.
844
879
.
2.
Zhang
,
J.
,
Gu
,
H.
,
Zhou
,
H.
,
Zhang
,
S.
, and
Laird
,
C.
,
1989
, “
Tensile Deformation and Fracture in High Purity Titanium: In Situ Observation by Scanning Electron Microscopy
,”
Mater. Sci. Eng., A
,
114
, pp.
89
96
.
3.
Zhang
,
J.
,
Gu
,
H.
,
Zhou
,
H.
,
Zhang
,
S.
, and
Laird
,
C.
,
1989
, “
Substructures and Their Changes in High Purity Titanium During Tensile Deformation
,”
Mater. Sci. Eng., A
,
119
, pp.
33
39
.
4.
Yang
,
Y.
,
Wang
,
L.
,
Zambaldi
,
C.
,
Eisenlohr
,
P.
,
Barabash
,
R.
,
Liu
,
W.
,
Stoudt
,
M. R.
, and
Crimp
,
M. A.
,
2011
, “
Characterization and Modelling of Heterogeneous Deformation in Commercial Purity Titanium
,”
JOM
,
63
(
9
), pp.
66
73
.
5.
Yang
,
Y.
,
Wang
,
L.
,
Bieler
,
T. R.
,
Eisenlohr
,
P.
, and
Crimp
,
M. A.
,
2011
, “
Quantitative Atomic Force Microscopy Characterization and Crystal Plasticity Finite Element Modeling of Heterogeneous Deformation in Commercial Purity Titanium
,”
Metall. Mater. Trans., A
,
42
(3), pp.
636
644
.
6.
Abe
,
T.
,
Nagaki
,
S.
, and
Akase
,
T.
,
1984
, “
Material Inhomogeneity and Surface Roughening During Plastic Deformation
,”
Trans. Jpn. Soc. Mech. Eng., A
,
50
(454), pp.
1236
1244
.
7.
Salem
,
A. A.
,
Kalidindi
,
S. R.
, and
Semiatin
,
S. L.
,
2005
, “
Strain Hardening Due to Deformation Twining in α-Titanium: Constitutive Relations and Crystal-Plasticity Modeling
,”
Acta Mater.
,
53
(
12
), pp.
3495
3502
.
8.
Salem
,
A. A.
,
Kalidindi
,
S. R.
,
Doherty
,
R. D.
, and
Semiatin
,
S. L.
,
2006
, “
Strain Hardening Due to Deformation Twining in α-Titanium: Mechanisms
,”
Metall. Mater. Trans., A
,
37
(1), pp.
259
268
.
9.
Wu
,
X.
,
Kalidindi
,
S. R.
,
Necker
,
C.
, and
Salem
,
A. A.
,
2007
, “
Prediction of Crystallographic Texture Evolution and Anisotropic Stress-Strain Curves During Large Plastic Strains in High Purity α-Titanium Using a Taylor-Type Crystal Plasticity Model
,”
Acta Mater.
,
55
(
2
), pp.
423
432
.
10.
Wouters
,
O.
,
Vellinga
,
W. P.
,
van Tijum
,
R.
, and
de Hosson
,
J. Th. M.
,
2005
, “
On the Evolution of Surface Roughness During Deformation of Polycrystalline Aluminum Alloys
,”
Acta Mater.
,
53
(
15
), pp.
4043
4050
.
11.
Wouters
,
O.
,
Vellinga
,
W. P.
,
van Tijum
,
R.
, and
de Hosson
,
J. Th. M.
,
2006
, “
Effect of Crystal Structure and Grain Orientation on the Roughness of Deformed Polycrystalline Metals
,”
Acta Mater.
,
54
(
10
), pp.
2813
2821
.
12.
Furushima
,
T.
,
Masuda
,
T.
,
Manabe
,
K.
, and
Alexandrov
,
S.
,
2011
, “
Prediction of Free Surface Roughening by 2D and 3D Model Considering Material Inhomogeneity
,”
J. Solid Mech. Mater. Eng.
,
5
(
12
), pp.
978
990
.
13.
Shawish
,
S. E.
, and
Cizelj
,
L.
,
2016
, “
Numerical Investigation of Grain Misorientations at and Close to the Free Surface of FCC Polycrystalline Metals
,”
Comput. Mater. Sci.
,
113
, pp.
133
142
.
14.
Tada
,
N.
,
Yagi
,
N.
,
Shimizu
,
I.
, and
Uchida
,
M.
,
2009
,
Regional Identification by Digital Height Correlation of Nanolevel Surface Profile
,”
SEM Fall Symposium and Workshop
, Columbia, SC, Oct. 5–7, p.
15
.
15.
Tada
,
N.
,
Uchida
,
M.
, and
Uenoyama
,
Y.
,
2012
, “
Non-Destructive Crack Detection by Nanometric Change in Surface Profile Using Digital Holographic Microscope
,”
ASME
Paper No. PVP2012-57299.
16.
Wang
,
L.
,
Barabash
,
R. I.
,
Yang
,
Y.
,
Bieler
,
T. R.
,
Crimp
,
M. A.
,
Eisenlohr
,
P.
,
Liu
,
W.
, and
Ice
,
G. E.
,
2011
, “
Experimental Characterization and Crystal Plasticity Modeling of Heterogeneous Deformation in Polycrystalline α-Titanium
,”
Metall. Mater. Trans., A
,
42
(3), pp.
626
635
.
You do not currently have access to this content.