Deformation and damage behavior of a 1070 steel (class U wheel steel) under thermo-mechanical and isothermal loading have been examined. Fatigue lives under thermo-mechanical and isothermal loading were compared for similar conditions of strain and temperature. For most cases, maximum tensile stresses developed in thermo-mechanical tests exceeded those obtained under isothermal conditions (at Tmin) for the same strain amplitude. Cyclic hardening was observed at 200 to 300°C in isothermal tests. Under thermo-mechanical loading, static strain aging resulted in added hardening due to alternate exposure of the material to high and low temperatures. When thermal recovery effects become dominant at the high temperature end, strengthening upon cooling was suppressed. Oxide scales readily formed at high temperatures (≥400°C) and resulted in an increase in damage accumulation rates. Oxygen penetration into crack flanks and the ensuing loss of carbon was identified using Auger spectroscopy. The severity of oxide penetration into the base metal increased with increase in surface crack density, longer oxidation times and higher temperatures.
Skip Nav Destination
Article navigation
April 1986
Research Papers
Observations of Material Behavior Under Isothermal and Thermo-Mechanical Loading
Huseyin Sehitoglu,
Huseyin Sehitoglu
Department of Mechanical and Industrial Engineering, University of Illinois at Urbana-Champaign, 1206 West Green Street, Urbana, IL 61801
Search for other works by this author on:
M. Karasek
M. Karasek
Department of Mechanical and Industrial Engineering, University of Illinois at Urbana-Champaign, 1206 West Green Street, Urbana, IL 61801
Search for other works by this author on:
Huseyin Sehitoglu
Department of Mechanical and Industrial Engineering, University of Illinois at Urbana-Champaign, 1206 West Green Street, Urbana, IL 61801
M. Karasek
Department of Mechanical and Industrial Engineering, University of Illinois at Urbana-Champaign, 1206 West Green Street, Urbana, IL 61801
J. Eng. Mater. Technol. Apr 1986, 108(2): 192-198 (7 pages)
Published Online: April 1, 1986
Article history
Received:
March 22, 1985
Online:
September 15, 2009
Citation
Sehitoglu, H., and Karasek, M. (April 1, 1986). "Observations of Material Behavior Under Isothermal and Thermo-Mechanical Loading." ASME. J. Eng. Mater. Technol. April 1986; 108(2): 192–198. https://doi.org/10.1115/1.3225860
Download citation file:
Get Email Alerts
Design and Development of Novel Lattice Structures for Optimum Energy Absorption
J. Eng. Mater. Technol (July 2024)
Related Articles
Thermomechanical and Isothermal Fatigue Behavior of Bare and Coated Superalloys
J. Eng. Mater. Technol (January,1996)
Thermo-Mechanical Fatigue of Mar-M247: Part 1—Experiments
J. Eng. Mater. Technol (January,1990)
Constitutive Modeling of Inelastic Solids for Plastic Flow Processes Under Cyclic Dynamic Loadings
J. Eng. Mater. Technol (April,1999)
A Mechanism-Based Approach From Low Cycle Fatigue to Thermomechanical Fatigue Life Prediction
J. Eng. Gas Turbines Power (July,2016)
Related Chapters
Clinical issues and experience
Mechanical Blood Trauma in Circulatory-Assist Devices
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Microstructure Evolution and Physics-Based Modeling
Ultrasonic Welding of Lithium-Ion Batteries