Detailed metallographic investigations of Gleeble simulated HAZ samples in modified 800H were performed. Precipitate dissolution, gain growth, HAZ liquation and the hardness degradation behavior in modified 800H were also addressed. Results of this study agree with previous HAZ hot cracking and softening behavior evaluations.